You are here: Home » Pressure Vessel » Lined Steel Vessels » 1000L Vertical Flat Bottom Steel Lined Plastic LLDPE Tank for Storage HCl (max 35%) , Naoh (max 50%) , Naclo (max 10%)

1000L Vertical Flat Bottom Steel Lined Plastic LLDPE Tank for Storage HCl (max 35%) , Naoh (max 50%) , Naclo (max 10%)

5 0 Reviews
Share to:
facebook sharing button
twitter sharing button
line sharing button
wechat sharing button
linkedin sharing button
pinterest sharing button
whatsapp sharing button
kakao sharing button
  • Metal Tank

Availability:
Quantity:
Customizing For Steel Lined Plastic LLDPE 1000L Vertical Flat Bottom Steel Lined Plastic LLDPE Tank For Storage HCl (max 35%) , Naoh (max 50%) , Naclo (max 10%)
Electrolytic Polishing Tank / Can /Pool Pipe Unit, Electrolytic Cleaning Tank,Acid Polishing Tank
1000L Vertical Flat Bottom Steel Lined Plastic LLDPE Tank for Storage HCl (max 35%) , Naoh (max 50%) , Naclo (max 10%)1000L Vertical Flat Bottom Steel Lined Plastic LLDPE Tank for Storage HCl (max 35%) , Naoh (max 50%) , Naclo (max 10%)1000L Vertical Flat Bottom Steel Lined Plastic LLDPE Tank for Storage HCl (max 35%) , Naoh (max 50%) , Naclo (max 10%)1000L Vertical Flat Bottom Steel Lined Plastic LLDPE Tank for Storage HCl (max 35%) , Naoh (max 50%) , Naclo (max 10%)

1000L Vertical Flat Bottom Steel Lined Plastic LLDPE Tank for Storage HCl (max 35%) , Naoh (max 50%) , Naclo (max 10%)1000L Vertical Flat Bottom Steel Lined Plastic LLDPE Tank for Storage HCl (max 35%) , Naoh (max 50%) , Naclo (max 10%)1000L Vertical Flat Bottom Steel Lined Plastic LLDPE Tank for Storage HCl (max 35%) , Naoh (max 50%) , Naclo (max 10%)

Metal cans Steel-Lined Plastic Square Tank, Electrolytic Tank, Pickling Tank Acid Containment Vessels Custom Made Rotationally Molded Linear Resins LLDPE
Custermizing Checmial Acid Storage Tank 1-150 m3 Steel Lined LLDPE Tank Used to Contain: HCl (max 35%) , Naoh (max 50%) , Naclo (max 10%) , PAC (max 17%) ,H2so4

Used to contain: HCl (max 35%), NaOH (max 50%), NaCLO (max 10%), PAC (max 17%), H2SO4 etc


Media (density) : (1155 Kg/m3), Hydrochloric Acid (1150 Kg/m3), Sulfate, Nitrate (1152 Kg/m3), Phosphate (1151 Kg/m3), Hydrofluoric Acid (1132 Kg/m3), Battery Fluid (1135 Kg/m3), Chloride (1135 Kg/m3), Ferric Chloride Solution (1130 Kg/m3), Sodium Hypochlorite (1130 Kg/m3), Sulfurous Acid (1030 Kg/m3)

processing/storing; aluminum sulfate, ammonium sulfate, calcium chloride, ethylene glycol, ferric chloride, ferric sulfate, ferrous sulfate, hydrochloric acid, hydrofluoric acid, hydrofluosilicic acid, hydrogen peroxide, magnesium chloride, phosphoric acid, polymers, potassium hydroxide, or just plain water and we'll design the vessel(s) you require.

Horizontal / Vertical Storage HCL Acid Tanks Steel Lined LDPE
For Storage Bleach, Hydrochloric Acid, Ferric Chloride, Oilfield Chemicals, Corrosive Wastes And Other Hazardous Cargoes.
Steel ( 6 mm -8mm ) Lined PE Plastic 7042 (16mm - 25 mm ) storage tank

Steel Lined LDPE aslo for Steel Lined LDPE Tank aslo for HCL(max 35%), NaOH (max 50%), NaCLO (max 10%), PAC (max 17%),H2SO4(60%,98%) ,HF (48%),H3PO4 (10%-85%),NH3. H2O,H2O2 (30%) Hazardous LiquidsTank Container

Steel Lined LDPE aslo for HCL(max 35%), NaOH (max 50%), NaCLO (max 10%), PAC (max 17%),H2SO4(60%,98%) ,HF ( 48%),H3PO4 (10%-85%),NH3. H2O,H2O2 (30%)
Compounds, cleaning liquid, UN1760,
Corrosive liquid, acidic, inorganic, n.o.s., UN3264,
Corrosive liquid, acidic, organic, n.o.s., UN3265,
Corrosive liquid, basic, inorganic, n.o.s., UN3266,
Hypochlorite solutions, UN1791,
Hydrochloric acid solution, UN1789,
Sulfuric acid, UN2796,
BATTERY FLUID, ALKALI UN 2797,

Detail Picture




1000L Vertical Flat Bottom Steel Lined Plastic LLDPE Tank for Storage HCl (max 35%) , Naoh (max 50%) , Naclo (max 10%)
Certifications

1000L Vertical Flat Bottom Steel Lined Plastic LLDPE Tank for Storage HCl (max 35%) , Naoh (max 50%) , Naclo (max 10%)

Packaging & Shipping

1000L Vertical Flat Bottom Steel Lined Plastic LLDPE Tank for Storage HCl (max 35%) , Naoh (max 50%) , Naclo (max 10%)

FAQ

1.Are you trading company or manufacturer ?

We are Group Corporation manufacturer ,have Group Factories Contractor.

2 .Can I have samples of this type of product to test the quality?
Yes, you can buy any sample to test the quality,our MOQ is 1 unit.

3. What's the delivery time and can you lower the price?
It depends on your order.The delivery time is within 30 workdays after we received your prepayment. If you have placed an order of large quantities, then,of course, the price can be lowered.
4.Can you supply some quick-wear parts?
Yes, we can supply the parts as your request,such as traction,traction pin,balance beam and plate spring,hanging accessories,turntable,all kinds of brake pads,brake pan, bearings,etc.
6.Do you have any used products for sale?
We have products in stock for choices,the prices are favorable,we'll show you our stock products if you need.

7.What's the payment terms?
TT 30% as deposit, balance before shipment by TT or at sight.

8. How to guarantee customers get the goods smoothly after they payment?
Don't worry,dear.We have joined the trade assurance,you can place the order by trade assurance,if we don't delivery products, the deposit will be returned to you.

9.How can you ensure the quality of the products?

Don't worry,dear.We have joined the trade assurance,if the products have quality problems when you received them,the payments can be refund to you.


There are five commonly used wrecker tow truck , usually depending on the type or size of the recovery wrecker :
First type : Boom towing truck

- use adjustable arms and winches to retract vehicles from ditches, embankments, or any vehicle that cannot arrive safely. Some booms are fixed, some heavy rotating racks, hydraulic telescopic tubes, others. In the past boom, trucks used the "hook chain" system, the chain around the frame or axle, and then hoisted by the winch. A heavy rubber pad is attached to the truck and truck so that it can be towed onto other bridges." Slings and belts are an evolution, replacing parts of chains with rubber belts. slings did not use too much today because they could shave bumper cars. But they are sometimes used in wrecker accidents carrier or have one or two front wheels or rear wheels missing or pickups and other vehicles have steel bumpers. Equipped with all wheel drive, the truck is towed away, unable to use the machine string, because it can make the car power transmission system problems.

Second type :Wheel lift wrecker towing truck

(also called "glasses") - from the chain hook technique to generate a large metal frame, can be installed in the front or rear under the cradle, rendering vehicles by pneumatic or hydraulic hoist can drag the ground clear front or rear. The device usually picks up the wheel of the vehicle (i.e., front wheel, if it is front wheel drive, rear wheel, if it is rear wheel drive), and contacts the tire. wheel lift wrecker tow truck are common in china; cradles are like glasses. Medium and heavy-duty trucks use variations, "underlift" or "chassis lift", in which the elevator shaft or frame is not the wheel. A forklift truck can be used as an adapter or a lift chassis.

Third type :Integration towing truck (also known as "Self Loader wrecker equipment", "Snatcher towing vehicle", "quick choice tow truck" or "roll back wrecker") - the arm and wheel lift together. Used of light trucks to recover or stop vehicles. Most of the truck's cab equipment is controlled so that the pickup truck does not leave the truck to connect the vehicle. heavy trucks are also manufactured using integrated lifts.

Forth type --Flat plates wrecker truck (also known as "rolling back tow truck" or "sliding tow truck") - the entire back of the truck is fitted with a bed that can be hydraulically tilted down to the ground, allowing the vehicle to be placed under its own power or pulled up by the winch. [9] because they carry, rather than traction vehicles, it can be completely fixed; in the United States, they carry serious damage to car accidents.

Fifth type ---Lifting platform wrecker truck the derricks lift the vehicle vertically and use the wheel lift to load it on the bed. In Europe, this car can eliminate the parallel parking of vehicles.



1000L Vertical Flat Bottom Steel Lined Plastic LLDPE Tank for Storage HCl (max 35%) , Naoh (max 50%) , Naclo (max 10%)



1000L Vertical Flat Bottom Steel Lined Plastic LLDPE Tank for Storage HCl (max 35%) , Naoh (max 50%) , Naclo (max 10%)

Rotationally Molded LLDPE TANK
chemical resistance of LLDPE
Cell / :+8615271357675
tictrucks.en.made-in-china.com

LDPE / HDPE Chemical Resistance Chart

The chemical compatibility of LDPE and HDPE on this chart is tested at 20°C: and 50°C: for 7 days and 30 days (if applicable) with constant exposure.

LDPE & HDPE resistance listed by chemical
1.4-dioxane LDPE / HDPE at 20°C: little or no damage after 30 days.
LDPE at 50°C: shows some effect after 7 days.
Acetaldehyde LDPE / HDPE at 20°C: little or no damage after 30 days.
HDPE at 50°C: shows some effect after 7 days.
LDPE at 50°C: immediate damage may occur.
Acetic Acid 5 % LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Acetic Acid, glacial 50% LDPE / HDPE at 20°C: little or no damage after 30 days.
LDPE at 50 °C: immediate damage may occur.
Acetone LDPE / HDPE at 20°C-50°C: damage may occur.
Not recommended for continuous use.
Allyl Alcohol LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Aluminum salts LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Amino acids LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Ammonia LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Ammonium carbonate saturated LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Ammonium phosphate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Ammonium sulphate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Amyl chloride HDPE at 20°C: shows some effect after 7 days.
HDPE at 50°C & LDPE at 20°C-50°C: immediate damage may occur.
Not recommended for continuous use.
Aniline LDPE / HDPE at 20°C: little or no damage after 30 days.
HDPE at 50°C: shows some effect after 7 days.
Benzene LDPE / HDPE at 20°C-50°C: damage may occur.
Not recommended for continuous use.
Benzyl alcohol LDPE / HDPE at 50°C: immediate damage may occur.
HDPE at 20°C: shows some effect after 7 days.
Boric acid LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Bromine LDPE / HDPE at 50°C: immediate damage may occur.
HDPE at 20°C: shows some effect after 7 days.
Butyric acid LDPE / HDPE at 50°C: immediate damage may occur.
HDPE at 20°C: shows some effect after 7 days.
Calcium chloride LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Calcium hydroxide saturated LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Carbon tetrachloride HDPE at 20°C: shows little or no damage after 30 days.
LDPE at 20°C & HDPE at 50°C: show some effect after 7 days.
LDPE at 50°C: not recommended.
Chlorine 10% in water LDPE / HDPE at 20°C: shows little or no damage after 30 days.
LDPE at 50°C: shows damage and is not recommended.
Chlorobenzene Immediate damage may occur.
Not recommended for continuous use.
Chloroform LDPE / HDPE at 20°C: show some effect after 7 days.
LDPE / HDPE at 50°C: immediate damage may occur.
Not recommended for continuous use.
Chromic acid 10% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Chromic acid 50% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Citric acid 10% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Cresol HDPE at 20°C: shows some effect after 7 days.
LDPE at 20°C-50°C & HDPE at 50°C: show immediate damage.
Not recommended for continuous use.
Cyclohexane LDPE / HDPE at 50°C: immediate damage may occur.
LDPE / HDPE at 20°C: show some effect after 7 days.
Diethyl ketone LDPE / HDPE at 20°C-50°C: damage may occur.
Not recommended for continuous use.
Dimethylsulfoxide LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Ethanol 95% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Ethyl acetate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Ethyl benzene HDPE at 20°C: shows some effect after 7 days.
LDPE at 20°C-50°C & HDPE at 50°C: show immediate damage.
Not recommended for continuous use.
Ethylene glycol LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Ethylene oxide HDPE at 20°C: shows little or no damage after 30 days.
LDPE at 20°C: and LDPE/ HDPE at 50°C: show some effect after 7 days.
Ferric chloride LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Fluoride LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Fluorine HDPE at 20°C: shows little or no damage after 30 days.
LDPE at 20°C: shows some effect after 7 days.
Not recommended at 50°C.
Formaldehyde 10% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Formaldehyde 40% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Glycerol LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Hexane HDPE at 20°C: shows little or no damage after 30 days continuous use.
HDPE at 50 °C: shows some effect after 7 days.
LDPE not recommended at any temperature.
Hydrochloric acid 20% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Hydrochloric acid 35% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Hydrochloric acid 5% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Hydrocyanic acid LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Hydrofluoric acid LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Hydrofluoric acid 4% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Hydrofluoric acid 48% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Hydrogen peroxide 3% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Hydrogen peroxide 30% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Isobutyl alcohol LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Isopropyl alcohol LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Kerosene LDPE / HDPE at 20°C: show some effect after 7 days.
LDPE / HDPE not recommended at 50°C, as immediate damage may occur.
Lactic Acid 10 % LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Lactic Acid 90 % LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Lead acetate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Methanol LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Methyl ethyl ketone Immediate damage may occur.
Not recommended for continuous use.
Methyl propyl ketone HDPE at 20°C: shows some effect after 7 days.
LDPE at 20°C-50°C & HDPE at 50°C: Immediate damage may occur.
Not recommended for continuous use.
Methylene chloride HDPE at 20°C: shows some effect after 7 days.
LDPE at 20°C-50°C & HDPE at 50°C: Immediate damage may occur.
Not recommended for continuous use.
Mineral oil LDPE / HDPE at 20°C: little or no damage after 30 days.
LDPE at 50°C: may show immediate damage and is not recommended.
n-amyl acetate LDPE / HDPE at 20°C: little or no damage after 30 days.
LDPE at 50°C: shows some effect after 7 days or constant exposure.
n-butyl alcohol LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Nitric acid 50 % LDPE at 20°C: shows little or damage after 30 days.
HDPE at 20°C & LDPE at 50°C: show effect after 7 days.
HDPE at 50°C: shows immediate damage and is not recommended.
Nitric acid 70 % LDPE / HDPE at 20°C: show some effect after 7 days.
LDPE / HDPE at 50°C: show immediate damage.
Not recommended.
n-octane LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Oleic acid HDPE at 20°C-50°C: little or no damage after 30 days.
LDPE at 20°C-50°C: shows immediate damage and is not recommended.
Oxalic acid LDPE at 20°C: shows some effect after 7 days.
HDPE at 20°C and LDPE / HDPE at 50°C: shows little/ no damage after 30 days.
Ozone LDPE / HDPE at 20°C: little or no damage after 30 days.
LDPE / HDPE at 50°C: show immediate damage.
Not recommended.
Perchloric acid LDPE / HDPE at 20°C: little or no damage after 30 days.
LDPE / HDPE at 50°C: show immediate damage.
Not recommended.
Perchloric ethylene LDPE / HDPE at 20°C-50°C: show immediate damage.
Not recommended.
Phenol LDPE / HDPE at 20°C-50°C: show immediate damage.
Not recommended.
Phosphoric acid 10% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Phosphoric acid 85% LDPE / HDPE at 20°C: little or no damage after 30 days.
LDPE at 50°C: shows immediate damage and is not recommended.
Phosphorous trichloride LDPE / HDPE at 20°C: little or no damage after 30 days.
LDPE at 50°C: has no data available. HDPE at 50°C: shows some effect after 7 days.
Potassium carbonate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Potassium hydroxide 5 % LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Potassium hydroxide concentrated LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Potassium permanganate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Propylene glycol LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Pyridine Immediate damage may occur.
Not recommended for continuous use.
Salicylic acid, saturated LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Silver acetate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Silver nitrate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sodium carbonate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sodium chloride, saturated LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sodium dichromate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sodium hydroxide 1% LDPE at 20°C-50°C: shows little or no damage after 30 days.
HDPE at 20°C-50°C: shows some effect after 7 days.
Sodium hydroxide 50% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sodium hypochlorite 15% HDPE at 20°C-50°C: little or no damage after 30 days.
LDPE at 20°C: is suitable
but at 50°C: shows some effect after 7 days.
Sodium nitrate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sodium sulphate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sucrose LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sulfuric acid 20% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sulfuric acid 6% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sulfuric acid 60% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sulfuric acid 98% LDPE at 20°C-50°C: shows little or no damage after 30 days.
HDPE at 20°C: shows effect after 7 days.
Not recommended for use at 50°C.
Tannic acid LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Tetrahydrofuran LDPE / HDPE at 20°C: show some effect after 7 day of constant exposure.
LDPE / HDPE at 50°C: show immediate damage.
Not recommended.
Toluene LDPE at 20°C: show some effect after 7 day of constant exposure.
HDPE at 20°C-50°C & LDPE at 50°C: show immediate damage.
Not recommended.
Trichloracetic acid LDPE / HDPE at 20°C: show some effect after 7 day of constant exposure.
LDPE / HDPE at 50°C: show immediate damage.
Not recommended.
Trichlorethane Immediate damage may occur.
Not recommended for continuous use.
Turpentine oil LDPE / HDPE at 20°C: show some effect after 7 days.
LDPE / HDPE at 50°C: show immediate damage.
Not recommended.
Urea LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Xylene HDPE at 20°C: shows some effect after 7 day of constant exposure.
LDPE at 20-50°C and HDPE at 50°C: show immediate damage.
Not recommended.
Zinc chloride LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Previous: 
Next: 

Related Products

Contact

 Address: R 23, F4,New Factory (4), B1, Phase II, Dashu Industrial Village , Liufang Street ,Wuhan East Lake Hi-tech Development Zone, Wuhan City, Hubei Province,P.R.China
Keystone Vessel Manufacturing Co., Ltd  Add :No.333,2nd Youyi Road,Lishan Town, Sui County,Hubei Province.
Phones: +86-152-7135-7675    https://ks-vessel.com
Email: isotanks@foxmail.com jin@ks-vessel.com

Industrial Gas Cylinders

Copyright © 2023-2033 Keystone Vessel (Wuhan) Co., Ltd , Keystone Vessel Manufacturing Co., Ltd  All Rights Reserved  Hubei Dong Runze Special Vehicle Equipment Co.,Ltd
Leave a Message
Contact Us